Fabrication, microstructure, mechanical, and electrochemical properties of NiMnFeCu high entropy alloy from elemental powders
Kumar, Ashok; Mucalo, Michael R.; Bolzoni, Leandro; Li, Yiming; Kong, Fantao; Yang, Fei (MDPI AG, 2022)Transition metal based high entropy alloys (HEAs) are often used in electrocatalytic (water electrolysis) applications due to the synergistic effect operating among its constituent elements and unpaired electrons in d ... -
High temperature deformation behavior of Ti–46Al–2Cr–4Nb–0.2Y alloy
Kong, Fantao; Chen, Yuyong; Zhang, Deliang; Zhang, Shuzhi (Elsevier, 2012)The hot deformation characteristics of cast and hot isostatically pressed Ti-46Al-2Cr-4Nb-0.2Y (at%) alloy in the temperature range of 1100-1250°C and strain rate range of 0.01-1.0s -1 using hot compression tests were ... -
Interfacial microstructure and shear strength of Ti-6Al-4V/TiAl laminate composite sheet fabricated by hot packed rolling
Kong, Fantao; Chen, Yuyong; Zhang, Deliang (Elsevier, 2011)A two layer Ti-6Al-4V(wt%)/Ti-43Al-9V-Y(at%) laminate composite sheet with a uniform interfacial microstructure and no discernible defects at the interfaces has been prepared by hot-pack rolling, and its interfacial ... -
Microstructure and mechanical properties of large size as-cast Ti-43Al-9V-0.2Y (at.%) alloy ingot from brim to centre
Kong, Fantao; Xu, Xingchen; Chen, Yuyong; Zhang, Deliang (Elsevier, 2011)A Ti-43Al-9V-0.2Y (at.%) alloy ingot with the size of Ф160×400mm was prepared by vacuum arc remelting (VAR). The microstructure of the as-cast Ti-43Al-9V-0.2Y alloy was composed of B2/α₂/γ lamellar colonies and massive B2 ... -
Microstructure and mechanical properties of large size Ti-43Al-9V-0.2Y alloy pancake produced by pack-forging
Su, Yongjun; Kong, Fantao; Chen, Yuyong; Gao, Na; Zhang, Deliang (Elsevier, 2013)A pancake of Ti-43Al-9V-0.2Y (at.%) alloy with dimensions of ϕ480 mm × 46 mm was fabricated by pack-forging with a thick reduction of 80%. The as-forged Ti-43Al-9V-0.2Y alloy pancake has a duplex (DP) microstructure, which ...